Permanent protection against graffiti. High degree of flexibility. Excellent weather resistance.
The enormously high chemical resistance, variety and functionality of our epoxy resin paints make this paint system a highly economical and very widely applicable interior coating. Helios epoxy resin powder coatings offer the highest level of corrosion protection and stone chip resistance. As a result, they have become indispensable, among other things, for painting underbody areas in vehicle construction. Thanks to their high reactivity, they can be fired in at low temperatures – resulting in abrasion-resistant surfaces.
You may download all information as data sheet (pdf):
Data sheet - PDF(113KB)
Applications
As primer to increase protection against corrosion, as single-layer solution for automotive suppliers, or as highly reactive NT powder coating.
Properties
Colour shade: all RAL, RDS, NCS, Pantone, Munsell etc. – also customer samples
Finish: smooth, fine texture, rough texture, thin film, and effects
Gloss: from flat to high gloss
Density: ca. 1,5 g/cm3, depending on colour shade and quality
Spreading rate: depends on the applied film thickness, c.f. formula
Storage life: average of 18 months
Coating properties
Erichsen cupping test: DIN EN ISO 1520, > 6 mm
Mandrel bend test: DIN EN ISO 1519, good over 10 mm mandrel
Salt spray test: DIN EN ISO 9227, > 650 hours without undercutting (corrosion creep) or blistering after appropriate pre-treatment
Condensation water test: DIN EN ISO 6270-2, > 650 hours without undercutting (corrosion creep) or blistering after appropriate pre-treatment
Resistance
Good regarding lye and acids – has to be tested individually
Processing
Finish: Aluminium, die-cast aluminium, steel – thorough degreasing required. To increase corrosion protection, a conversion layer is recommended.
Application: all common processes (Tribo, Corona)
Curing conditions: 7 minutes at 140 to 180 °C object temperature
Overcoatability: Can be overcoated with the same product or with special repair coatings.
Curing conditions
SERIE 05 EPOXIDHARZPULVERLACK – Einbrennfenster
Theoretical spreading rate
Values were calculated according to the following formula:
Theoretical spreading rate (m2)/(kg) = 1000 / density x film thickness
These data are based on empirical values for the completeness of which we do not assume any guarantee. Since we cannot influence in any way the processing of the product, the purchaser is responsible for ensuring that the product is suitable for the intended purpose before using the product. Any change in the processing procedure, environmental conditions, or the non-observance of instructions can influence the result negatively. Status per 07/2012.